Laserfiche WebLink
TECHNICAL DATA BULLETIN <br /> VersiWeld TPO Reinforced Membrane <br /> Typical Properties and Characteristics <br /> Physical Property ASTM 06878 45-mil 60-mil 80-mil EXTRA <br /> Requirement (1.14 mm) (1.52 mm) (2.03 mm) <br /> Tolerance on Nominal Thickness,% +13. -10 ± 10 t 10 10 <br /> ASTM D751 test method <br /> Thickness Over Scrim,in (mm) 0 015 min 0 018 typical 0 024 typical 0 034 typical <br /> ASTM D7635 optical method,average of <br /> 3 areas (0 380) (0 457) (0 610) (0 864) <br /> Breaking Strength,Ibf(M) 220(976 N) 225(1 0)min 250(1 1)min 350(1 6)min <br /> ASTM 0751 grab min 320(14)typical 360(1 6)typical 425(1 9)typical <br /> Elongation Break of Reinforcement% 15 min 15 min 15 min <br /> ASTM D751 grab method 15 min 25 typical 25 typical 25 ypical <br /> Tearing Strength,Ibf(N) 55(245)min 55(245)min 55(245)min <br /> ASTM D751 proc B 8 in x 8 in. 55(245)min 130(578)typical 130(578)typical 130(578)typical <br /> Brittleness Point°F('C) -40(-40)max -40(-40)max -40(-40)max <br /> ASTM D2137 40(•40)max -50(-46)ypical -50(-46)typical -50(-46)typical <br /> Linear Dimensional Change,% I-1 max ± I max ± 1 max <br /> ASTM D1204,6 hours at 158"F - Max -0 2 typical -0 2 typical -0 2 typica <br /> Ozone Resistance,no cracks 7X PASS PASS PASS PASS <br /> ASTM 01149, 100 pphm, 168 his <br /> UV Exposure(Xenon Arc),no cracks <br /> 7X ASTM 6155,min PASS PASS PASS PASS <br /> exposure 1Q080 Ulm' <br /> (4,000 hrs-0.70 W/m2) <br /> Water Absorption Resistance,mass% ±3 0 max -3 0 max t 3 0 max <br /> ASTM D471 top surface only 166 hours at _ }max 158°F water 0 90 typical 0 90 typical 0 90 tyoical <br /> Factory Strength,Ibf(N) <br /> ASTM p751 66(290)m n 66(290)min 66(290)min 66(290)min <br /> 51 grab method <br /> Field Seam Strength,Ibf/in(kN/m) 25(44)min 25(44)min 40(70)min <br /> ASTM 01876 tested in peel No requirement 50(8 8)typical 60(10 5)typical 70(12 3)typical <br /> Water Vapor Permeance, Perms No requirement 010 max 010 max 010 max <br /> ASTM E96 proc B 005 typical 005 typical 005 typical <br /> Puncture Resistance,Ibf(M) 250 0 1)min 300(1 3)min 400(1 8)min <br /> FTM 101C,method 2031 No requirement <br /> (see supplemental section) 325(14)typical 350(1 6)typical 450(2 0)typical <br /> Properties After Near Aging <br /> ASTM D573,32 weeks @ 240'F orPAS pq PASS PASS <br /> 8 weeks in 27 Nn cr°ck.ng No cracking No crock ng No cracking <br /> No cracking when bent around _3°diameter mandrel 5❑,cx 10 Max 10 max 10 max <br /> Weight Change,% <br /> Typical Weignts loift'(k9/m2) 0 33`1 1) 029 -14) 0 40(2 0) <br /> icp cw aro,:rlies and;nomcren;ncs an bawd r:n,,iinpuy reeaeJ and arc:nor gormin'eed for nip;nripies of'h s Croducl this Join ann iN;;noi on is,r,btnded cis n jwda and dies nor <br /> rP.-3:, sUP�ili L'll•.Jr'r_ _I',r I""I:r';11ti t�.... ;;I 11',. „�1,:,. <br /> VERSICO <br /> ROOFING SYSTEMS <br />